SZUV-S9006 is an ABS like SL resin which has high-toughness features. It is designed for solid state SLA platforms. SZUV-S9006 can be applied in master patterns, concept models, assembly parts and functional prototypes in the field of automotive, medical and consumer electronics industries.The parts duability building with SZUV-S9006 is over 6.5months.SZUV-S9006
-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines
-Improved strength retained, improved dimensions retention of parts in humid condition
-need minimal part finishing
-Long shelf life in machine
-Low bottom contraction
-Need less part finishing time,easier post-curing
-Buliding accurate and high tough parts with an improved dimensional stability
-High quality controls for vacuum casting parts
-Low shrink and good resistance to yellowing
-Magnificent white color
-Outstanding machinable SLA material
Physical Properties – Liquid Material
|Density||1.11-~1.15g/cm3 @ 25 ℃|
|Viscosity||230~290cps @ 26 ℃|
|Building layer thickness||0.05~0.12mm|
|90-minute UV post-cure|
|Hardness, Shore D||ASTM D 2240||75~85|
|Flexural modulus, Mpa||ASTM D 790||2,592-2,675|
|Flexural strength, Mpa||ASTM D 790||63- 70|
|Tensile modulus, MPa||ASTM D 638||2,489-2,595|
|Tensile strength, MPa||ASTM D 638||36-53|
|Elongation at break||ASTM D 638||15 -25%|
|Poisson`s Ratio||ASTM D 638||0.4-0.44|
|Impact strength notched Izod, J/m||ASTM D 256||45 - 70|
|Heat deflection temperature, ℃||ASTM D 648 @66PSI||38~50|
|Coefficient of thermal expension||TMA(T<Tg)||90~102*E-6|
|Dielectric Constant60 Hz||ASTM D 150-98||4.2~5.0|
|Dielectric Constant 1 kHz||ASTM D 150-98||3.3~4.2|
|Dielectric Constant1 MHz||ASTM D 150-98||3.2~4.0|
|Dielectric StrengthkV/mm||ASTM D 1549-97a||12.8~16.1|
Fire Fighting Measures
Dry powder fire extinguishing agent, alcohol resistant foam extinguishing agent, carbon dioxide, dry sand, spray water.
Fires may produce irritation and harmful gas
（3）The firemen of protective measures
Fireman should wear protective appliances (eye protection, protective clothing, mailing gas with gas mask, etc.), put out the fire in the windward.
6.Accidental Release Measures
（1）Homework personnel protective equipment
Ensure adequate ventilation, wear suitable protective clothing, make a good job in hand and eye/face protection.
（2）Environmental protection measures
Prevent products from entering the drain or open water
For a small amount of leakage, use dry sand, soil and towels absorb the residual liquid, recycling and airtight container.
For a large number of leakage, leakage of liquid can be in front of the embankment, the introduction of recycle to safe place.
（4）Secondary hazard prevention measures
Quickly remove all fire spark (ban on smoking in nearby, and the ignition).
7.Handling And Storage
（1）Operation treatment technical measures
Avoid contact with eyes, skin and clothing. Don't inhaling mist or steam, don't accidentally swallow, keep container tightly closed after the thorough cleaning.
（2）Partial or full ventilation
Maintain adequate ventilation
（3）Safe handling matters needing attention
No smoke, no fire
（4）Safe storage conditions
Stored in a cool, well ventilated place, away from heat, sparks and flames. Keep container tightly closed until it is put into use.
（5）packaging container and material
In the process of custody, please do not transfer to other containers. Don't fall back to the original containers of products that will be used.